Nucleating Agent-Containing P(LLA-mb-BSA) Multi-Block Copolymers as Ultra-tough Bioplastics and High Performance Thermoplastic Elastomers with Balanced Mechanical Properties.  
Nucleating Agent-Containing P(LLA-mb-BSA) Multi-Block Copolymers as Ultra-tough Bioplastics and High Performance Thermoplastic Elastomers with Balanced Mechanical Properties.
资料类型: PDF文件
关键词: In  order  to  obtain  high  performance  bioplastics  
and  thermoplastic  elastomers  P(LLA-mb-BSA)  multi-block  copolymers  containing  
30  wt  %  and  70  wt  %  
soft  segment  (PLBSA30  and  PLBSA70  for  short)  
were  synthesized  via  chain  extension  and  coupling  
of  poly(L  
资料大小: 921k
所属学科: 通用高分子材料
来源: 来源网络
简介:
In order to obtain high performance bioplastics and thermoplastic elastomers, P(LLA-mb-BSA) multi-block copolymerscontaining 30 wt % and 70 wt % soft segment (PLBSA30 and PLBSA70 for short) were synthesized via chain extension and coupling ofpoly(L-lactic acid) (PLLA) and poly(butylene succinate-co-adipate) (PBSA) prepolymers in the presence of 1% nucleating agent (NA). Theywere characterized with proton nuclear magnetic resonance (1H NMR), gel permeation chromatography (GPC), differential scanningcalorimetry (DSC), polarizing optical microscopy (POM), thermal gravimetric analysis (TGA), transmission electron microscope (TEM),and tensile and impact test. The relatively high molecular weights of (Mn 8200 g/mol and 3100 g/mol for PLLA and PBSA, respectively) thepolyester sequences are helpful to improve the PLLA crystallization and the flexibility of the PBSA soft segment. Nucleation effect furtheraccelerates the crystallization of PLLA segment. The synergistic effect of these factors results in good balance between stiffness and toughness.PLBSA30s containing 1% zinc citrate (ZnCC) or talc behave as ultra-tough bioplastics with ultrahigh impact strength over 50 kJ/m2 andexcellent tensile properties. PLBSA70 containing 1% ZnCC possesses elongation at break of 600% and retains high modulus (56 MPa) andstrength (16 MPa) and therefore behaves as an excellent thermoplastic elastomer. The excellent and balanced properties would extend the end applications of these PLLA-based materials.
上传人: wulinbo
上传时间: 2017-09-01 16:16:22
下载次数: 0
消耗积分: 0  
立即下载:
1人
1人
1人
友情提示:下载后对该资源进行评论,即可奖励2分。
报告错误:  1.下载无效  2. 资料明显无价值  3. 资料重复存在

相关评论 共有0人发表评论 更多评论
你还没有登录,无法发表评论,请首先 登录 注册
免责声明:本站部分资源由网友推荐,来自互联网,版权属于原版权人,如果不慎侵犯到您的权利,敬请告知,我们会在第一时间撤除。本站中各网友的评论只代表其个人观点,不代表本站同意其观点。