  • Ni(II) and Pd(II) Complexes Bearing Novel Bis(b-ketoamino) Ligand and Their Catalytic Activity toward Copolymerization of Norbornene and 5-Norbornene-2-yl Acetate Combined with B(C6F5)3
  • 来源:王凯悌副教授个人网站 2022-07-14
  • Two complexes Mt{C10H8(O)C[N(C6H5)]CH3}2 [Mt =Ni(II); Mt = Pd(II)] were synthesized, and the solid-state structures of the complexes have been determined by single-crystal X-ray diffractions. Homopolymerization of norbornene (NB) and copolymerization of NB and 5-norbornene-2-yl acetate (NB-OCOCH3) were carried out in toluene with both the two complexes mentioned above in combination with B(C6F5)3. Both the catalytic systems exhibited high activity toward the homopolymerization of NB (as high as 2.7  105 gpolymer/molNi h, for Ni(II)/B(C6F5)3 and 2.1  105 gpolymer/molPd h for Pd(II)/ B(C6F5)3, respectively.). Although the Pd(II)/B(C6F5)3 shows very lower activity toward the copolymerization of NB with NBOCOCH3, Ni(II)/B(C6F5)3 shows a high activity and produces the addition-type copolymer with relatively high molecular weights (MWs; 1.80–2.79  105 g/mol) as well as narrow MW distribution (1.89–2.30). The NB-OCOCH3 content in the copolymers can be controlled up to 5.8–12.0% by varying the comonomer feed ratios from 10 to 50%. The copolymers exhibited high transparency, high glass transition temperature (Tg > 263.9  C), better solubility, and mechanical properties compared with the homopolymer of NB. The reactivity ratios of the two monomers were determined to be rNB-OCOMe ? 0.08, rNB ? 7.94 for Ni(II)/B(C6F5)3 system, and rNB-OCOMe ? 0.07, rNB ? 6.49, for Pd(II)/B(C6F5)3 system by the Kelen-Tu¨ do? s method.

  • [来源:中国聚合物网]
  • 了解更多请进入: 王凯悌副教授个人网站
相关新闻
  • · Electronic Modulation Induced Luminescence from Triphenylamine Derivative and Temperature Sensor Application
  • · Long-Lived Dynamic Room Temperature Phosphorescence from Carbon Dots Based Materials
  • · Simultaneously improving of thermal resistance and mechanical performances of cyclic olefin copolymers by incorporation of bulky adamantane side group
  • · Dual Promotion of Phosphorus Groups for Ultralong Room Temperature Phosphorescence with High Efficiency

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017