Carbon nanotubes preparation using carbon monoxide from the pyrolysis flame
关键词: carbon nanotube V-type pyrolysis flame temperatu
类 别: 橡胶 >> 橡胶原料
来 源: 2009高分子先进制造业论坛(青岛)
资料类型: pdf文件
资料大小: 485K
简 介: Carbon nanotube is a new kind of carbon material. Synthesis of carbon
nanotubes from V-type pyrolysis flame is a kind of novel technique. It needs simple
laboratory equipments and normal atmosphere pressure. The V-type pyrolysis flame
experimental system is introduced. Carbon source is the carbon monoxide which is
carried to the middle pipe of V-type pyrolysis flame combustor. Heat source is from
acetylene /air premixed flame. Pentacarbonyl iron, served as catalyst, is transported
by spray- pyrolysis method into the burner. The carbon nanotubes were characterized
by scanning electron microscope and transmission electron microscope. The diameter
of carbon nanotubes is approximate 20nm and its length is dozens of microns. The
impact of the temperature, reactant composition and catalyst was analyzed to reveal
the rule of carbon nanotube growth. Carbon nanotubes with good form and less
impurity can be captured when the temperature was from 800℃ to 1000℃ and carbon
monoxide/hydrogen/helium mixed gas flow was supplied. The effective diameter of
pentacarbonyl iron nanoparticles is approximate from 5nm to 20nm in the process of
carbon nanotube formation. Mechanism of carbon nanotube base on the V-type
pyrolysis flame method was proposed. The carbon “dissolved-proliferation-separate
out” theory can be used to explain how the pentacarbonyl iron catalyses carbon
monoxide to form carbon nanotubes.
上传人: chem2000
上传时间: 2009-11-04 16:21:55
下载次数: 1
消耗积分: 2
我要收藏:
 
友情提示:下载后对该资源进行评论,即可奖励2分。
好:
中:
差:
本栏目部分资源来自互联网,仅为促进数据共享和信息交流,如有版权问题请告知本网或上传者本人,本网会及时给予答复。
报告错误  1.下载无效  2. 资料明显无价值  3. 资料重复存在
评论:(共有0人发表评论) 更多>>
你还没有登录,无法发表评论,请首先