作者：Zhengguang Heng, Rui Li, Yang Chen*, Huawei Zou*, Mei Liang
关键字：Triblock copolymer, Epoxy, Mechanical properties, Damping property, Surface property
论文来源：期刊
具体来源：Journal of Polymer Research, 2016, 23(7): 1-10.
发表时间：2016年

ABSTRACT: Amphiphilic triblock copolymer Poly(ε-caprolactone)-block-polydimethylsiloxane-block-poly(ε-caprolactone) (PCL-b-PDMS-b-PCL, LDL) was synthesized via the ring-opening polymerization of ε-caprolactone in the presence of hydroxyl-terminated polydimethylsiloxane

(HTPDMS) and was utilized to modify epoxy. The tensile strength and elongation at break were simultaneously enhanced when the triblock copolymer was incorporated. With increasing the concentration of the triblock copolymer, the damping temperature range (tanδ >0.25) was broadened from 21 °C to 34.5 °C. Meanwhile, the storage modulus of the composites and the values of tanδ had no significant decrease. When the concentration of the triblock copolymer was 20 wt%, the value of KIC attained 1.68 MN/m3/2, which was 1.56 times that of the neat epoxy (1.08 MN/m3/2). Besides, the characterization of hydrophobic and hydrophilic performance indicated that the incorporation of the triblock copolymer made epoxy resins transformed from hydrophilic to hydrophobic. It is expected that damping composites obtained by this method may be used as damping structural integration materials in future.