Control of carbon nanotubes at the interface of a co-continuous immiscible polymer blend to fabricate conductive composites with ultralow percolation thresholds
作者:Jinrui Huang, Cui Mao, Yutian Zhu*, Wei Jiang, Xiaodong Yang
关键字:conductive polymer composites, ultralow percolation thresholds, carbon nanotubes
论文来源:期刊
具体来源:Carbon
发表时间:2014年
The concept of ‘‘double percolation’’, i.e., conductive fillers are selectively located in one
phase of a co-continuous polymer blend to form a percolated network in the selected
phase, is widely used to reduce the percolation thresholds of conductive polymer composites
to a fraction of their original values. However, it is expected that the percolation threshold
can be significantly reduced further if the conductive fillers are only selectively
distributed at the continuous interface of the co-continuous polymer blend, where only a
very small amount of fillers are needed to build up the conductive percolated network. Multiwalled carbon nanotubes (MWCNTs) with very high aspect ratio (ca. 1000) are selectively distributed at a continuous interface of a co-continuous immiscible poly(lactic acid)/poly(ecaprolactone) (PLA/PCL) blend at a weight ratio of 50/50 by controlling the migration process of MWCNTs from the unfavorable PLA to the favorable PCL phase. Compared to the PLA/PCL/MWCNTs composites by the traditional double percolation method (percolation threshold is ca. 0.97 wt%), the percolation threshold of PLA/MWCNTs/PCL composites (ca. 0.025 wt%) drops 2 orders of magnitude due to controlling the MWCNTs at the continuous interface between the PLA and PCL phases.