作者：Zhaohua Xu, Yanhua Niu, Zhigang Wang, Heng Li, Liang Yang, Jie Qiu and Howard Wang
关键字：聚乳酸，结晶，碳纳米管，长径比
论文来源：期刊
具体来源：ACS Appl Mater Interfaces 2011，3 (9)，3744-3753.
发表时间：2011年

Biodegradable polylactide (PLA) composites added with acid oxidized multiwalled carbon nanotubes (AMWCNTs) of two different aspect ratios (length to diameter)
were prepared by coagulation. The aspect ratios and surface structures of A-MWCNTs were characterized by TGA, Raman, and SEM measurements. The percolation thresholds for gelation in the PLA composites with A-MWCNTs of large and small aspect ratios are 2.5 and 4.0 wt %, respectively, which were
determined by a rheological method, and in turn, the rheological
result confirms the aspect ratio differences for the added two types of A-MWCNTs in the composites. Isothermal crystallization kinetics of neat PLA and its composites were further investigated by using polarized optical microscope (POM)
and differential scanning calorimetry (DSC) to clarify the effects of A-MWCNTs of different aspect ratios and concentrations. The different aspect ratio A-MWCNTs with the same carboxyl group mass percent show substantial effects on PLA crystallization kinetics. Those with smaller aspect ratios enhance nucleation rate for PLA spherulites much more than those with larger aspect ratios. This phenomenon can be attributed to fewer sidewall carboxyl groups on the surfaces of A-MWCNTs with smaller aspect ratios, which provides more nucleation sites for PLA crystallization than those with larger aspect ratios at the same concentration, resulting in faster PLA nucleation rates for the former one.