Significantly Accelerated Spherulitic Growth Rates for
Semicrystalline Polymers through the Layer-by-Layer Film Method
Yaqiong Zhang,? Hongjun Xu,? Jingjing Yang,? Shouyu Chen,? Yunsheng Ding,? and Zhigang Wang*,?
?CAS Key Laboratory of Soft Matter Chemistry, Department of Polymer Science and Engineering, Hefei National Laboratory for
Physical Sciences at the Microscale, University of Science and Technology of China, Hefei, Anhui Province 230026, P. R. China
?Institute of Polymer Materials & Chemical Engineering, School of Chemical Engineering, Hefei University of Technology, Hefei,
Anhui Province 230009, P. R. China
摘要：很少有人思考过一层液态聚合物铺敷在结晶聚合物表面会起到什么样的效果。在这篇文章所报道的研究中我们主要是以偏光显微镜（POM）观察一层聚环氧乙烷（PEO）膜覆盖在聚乳酸（PLA）膜表面上，PEO熔体层对PLA在不同温度下等温结晶动力学的影响。我们将该PEO/PLA双层膜与PLA膜和PLA/PEO共混物膜中PLA结晶动力学行为进行了对比研究。非常有意思的是PEO熔体层可以显著加快PLA球晶的生长速率。另一个重要发现是双层膜中PLA竟然可以在接近PLA的玻璃化转变温度（Tg）处发生结晶。我们用调试差示扫描量热法（MDSC）和动态机械分析法(DMA)分别测量PEO/PLA双层膜的Tg变化, 由于PEO层的影响，PLA的Tg仅有轻微下降。我们用扫描电子显微镜(SEM)观察了双层膜的断面，发现在PLA和PEO层间有不规则的界面扩散层，该扩散层对加快PLA球晶生长速率起着很大的作用。我们的研究结果表明其实可以用这种多层膜方法来代替共混法进行聚乳酸等结晶聚合物的加工，减低能耗, 该方法有极大的潜在应用价值。