Tailoring microstructure and mechanical properties of injection molded isotactic–polypropylene via high temperature preshear
writer:Baobao Chang, Bo Wang, Guoqiang Zheng(通讯作者), Kun Dai, Chuntai Liu Changyu Shen.
keywords:isotactic–polypropylene
source:期刊
specific source:Polymer Engineering and Science, 2015, 55, 2714-2721.
Issue time:2015年

In this work, isotactic–polypropylene (iPP) specimens were prepared by a modified injection molding machine, in which high temperature preshear (HTPS) can be imposed on the molten polymer during the plasticizing stage. The effect of HTPS on the microstructure and mechanical property of iPP was investigated. It was found that spherulite size in core region of iPP part decreased steadily with the increasing HTPS duration, indicating that HTPS could substantially enhance iPP nucleation. Moreover, b-iPP formation correlated strongly with HTPS duration. That is, in the absence of HTPS, b-iPP existed only in intermediate region; with moderate HTPS duration, b-iPP could be unexpectedly formed in core region; however, long HTPS duration inhibited b-iPP formation in both intermediate region and core region. Based on the relationship between b-iPP formation and HTPS duration, metastable nuclei, instead of a-row nuclei, were proposed to be responsible for the development of b-iPP. Notched Izod

impact test showed that moderate HTPS duration enhance the impact strength of injection molded iPP by decreasing the thickness of shear region and elevating biPP crystallinity in core region. Dynamic mechanical test indicated that with the increase of HTPS duration, the storage modulus of injection-molded iPP improves drastically.