作者：Jie Zhao, Li Ma, Xiaojun Wang, Anthony Meyer, Weihua Ming*
关键字：Antifogging，Frost-resistan
论文来源：期刊
发表时间：2015年
We prepared an effective antifogging/frost-resisting coating by forming a semi-interpenetrating polymer network (SIPN) on the basis of a linear, random terpolymer poly(2-(dimethylamino)ethyl methacrylate-co-N-vinylpyrrolidone-co-methyl methacrylate), poly(DMAEMA-co-NVP-co-MMA), and a network of poly(ethylene glycol dimethacrylate). The excellent antifogging/frost-resisting property was mainly attributed to a balanced hydrophilicity/hydrophobicity of the terpolymer with the optimal DMAEMA/NVP/MMA molar ratio at 40/30/30. Compared to our previous work using poly(DMAEMA-co-MMA), the terpolymer-based coating demonstrated excellent antifogging property against both low- and high-temperature moist air, by eliminating the lower critical solution temperature related to the DMAEMA segments in the binary copolymer. By monitoring the coating thickness change during the fogging/frosting test, it appeared that water molecules could rapidly be absorbed into and desorbed from the terpolymer-based coating, implying long-term effectiveness of the antifogging/frost-resisting coating.