【Applied Surface Science】Investigation on surface layer characteristics of shot peened graphene reinforced Al composite by X-ray diffraction method
作者：Ke Zhan, Yihao Wu, Jiongli Li, BinZhao, YaYan, Lechun Xie, Lianbo Wang, V.Ji
关键字：Graphene, Al composite
论文来源：期刊
具体来源：Applied Surface Science, 435: 1257-1264.
发表时间：2017年
Graphene reinforced Al composite with high mechanical property was successfully reported. However, there are quite limited studies about shot peening effect on this new type material. Here, 1.0?wt% graphene reinforced Al composite was produced by powder metallurgy and treated by shot peening. The surface layer characteristics of shot peened composite was investigated by X-ray diffraction line profile analysis. The microstructure including domain size, micro-strain, dislocation density and crystalline texture were analyzed. The results showed that after surface shot-peening, the domain size were refined, the dislocation density of the composite was increased sharply to 9.0?×?1011/cm2 at the top surface. The original strong texture was diminished after shot peening. Based on the calculated results, the microstructure variation of composite was more severe than that of Al without graphene reinforcement after shot peening. Besides, the micro-hardness of composite at the top surface increased up to 75HV one time higher than that of matrix. It is concluded that shot peening can be considered as an essential process of improving the surface properties of graphene reinforced Al composite.