作者：唐武飞,张胜,孙军, 李洪飞, 刘晓东, 谷晓昱
关键字：the Fire Performance of Polypropylene Composite
论文来源：期刊
发表时间：2016年
Modified kaolinite containing Lewis acidic sites (Acid-Kaol) was prepared by calcination of kaolinite (Kaol) and successive acid treatment. Acid-Kaol was then introduced into polypropylene (PP) with intumescent flame-retardant (IFR). The flammability and thermostability of PP/IFR/Acid-Kaol were studied by limiting oxygen index (LOI), vertical buring test (UL-94), cone calorimeter test (CCT) and thermogravimetric analysis (TGA). LOI value ofPP/25 wt.% IFR composite was 31.1%, it increased to 34.9% by 1.5 wt.% Acid-Kaol substitution with IFR. Moreover,the peak of heat release rate (PHRR) of PP/IFR/Acid-Kaol decreased 46.8% compared with that of PP/IFR composite.The residues after CCT were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectrometer (XPS) and FTIR. It was indicated that Acid-Kaol accelerated crosslinking during combustion and promoted char formation, which will act as insulating barrier to protect the matrix from further decomposed. © 2016 Elsevier B.V.