【 Sensors & Actuators B Chemical】Preparation of anti-nonspecific adsorption polydopamine-based surface protein-imprinted magnetic microspheres with the assistance of 2-methacryloyloxyethyl phosphorylcholine and its application for protein recognitio
作者:Xiangjie Li, Jingjing Zhou, Lei Tian, Yufei Wang, Baoliang Zhang, Hepeng Zhang, Qiuyu Zhang
关键字:Protein imprinting; Anti-nonspecific adsorption; 2-Methacryloyloxyethyl phosphorylcholine; Polydopamine; Recognition specificity
论文来源:期刊
具体来源:http://www.sciencedirect.com/science/article/pii/S0925400516317324
发表时间:2017年

A new anti-protein nonspecific adsorption polydopamine-based surface protein-imprinted magnetic microsphere was prepared by using surface imprinting and AGET-ATRP in this work. The highlights were as follows. Firstly, different from our previous work, we could guarantee that there was no anti-protein nonspecific adsorption MPC chain segment in the imprinted sites. This fact could eliminate the negative influence of MPC chain segment on imprinted sites and further ensure the high imprinting efficiency. Secondly, the length of MPC chain segment was optimized to weaken the influence of protein resistance effect on adsorption capacity on the premise of guaranteeing excellent anti-protein nonspecific adsorption. The results showed that the optimal dopamine layer thickness was 10 nm. The mass ratio of MPC and Fe3O4@SiO2@Pdop-MIPs-Br was determined as 12/1. Under such conditions, after the graft of MPC, the adsorption capacity of imprinted microspheres for BSA decreased only a little from 9.39 mg/g to 8.26 mg/g, whereas the imprinting factor increased markedly from 1.53 to 5.74, revealing the advantage of this work. Finally, the successful applications in protein recognition showed that the new strategy was expected to be an effective means for improving the detection sensitivity of molecularly imprinted biosensors.