Fabrication of mono-dispersed cerium oxide nanopowders via mixed solvothermal route
作者：Wang, Fuxing，Wang, Zhifeng，Wu, Maoyan，Guo, Xunda，Wang, Chunhong，Zhang, Ming*
关键字：cerium dioxide, mixed solvothermal, particle size distribution, rare earths
论文来源：期刊
具体来源：Journal of Rare Earths
发表时间：2010年
Monodisperse and single-phase cerium oxide nanopowders were synthesized by mixed solvothermal route, Ce(NO3)3·6H2O as raw materials, poly (vinylpyrrolidone) (PVP) as stable agent. The cerium oxide nanopowders could be controlled from 50 to 60 nm by adjusting the ratio between ethanol absolute and water at 160 °C. With methanol instead of ethanol absolute, the reaction temperature could be lowered to 130 °C.