作者：Xiaoyun Liu, Hui Guo, Liusheng Zha
关键字：intelligent nanogels; interpenetrating polymer network structure; temperature stimulus responsiveness; pH stimulus responsiveness
论文来源：期刊
具体来源：Polymer International, 2012, 61:1144-1150
发表时间：2012年
Nanogels with interpenetrating polymer network (IPN) structure based on poly(N-isopropylacrylamide) (PNIPAM) and
poly(acrylic acid) (PAA) were synthesized by in situ polymerization of acrylic acid and N, N-methylenebisacrylamide within the PNIPAM nanogels. Their IPN structure was confirmed using transmission electron microscopy after staining by uranyl acetate. The temperature- or pH-dependent hydrodynamic diameters measured using dynamic laser light scattering show that the IPN nanogels have pH and temperature dual stimuli-responsive properties. As compared to previously reported pH/temperature dual stimuli-responsive nanogels, these IPN nanogels have the advantage of lessmutual interference between the temperature-responsive and pH-responsive components,which is beneficial for their applications in controlled drug release and sensors. The temperature- and pH-triggered volume phase transition mechanisms of the IPN nanogels were tested by probing the microenvironment change of their PNIPAM and PAA chains upon phase transition using infrared (IR) absorption spectra measured at different pH values and IR difference spectra obtained by subtracting the IR spectrum obtained before temperature-induced phase transition from that obtained after phase transition.