作者：Guangyu Liu, Xinlin Yang*, Yongmei Wang
关键字：Distillation precipitation polymerization; Silica/polymer core-shell composite; Hydrogen-bonding interaction
论文来源：期刊
具体来源：Polymer, 48 (15), 4385-4392 (2007). DOI: 10.1016/j.polymer.2007.05.060
发表时间：2007年
Monodisperse silica/poly(N,N0-methylenebisacrylamide) coreeshell composite materials with silica as core and poly(N,N0-methylenebisacrylamide) (PMBAAm) as shell were prepared by a two-stage reaction, in which the silica core with diameter of 500 nm was synthesized in the first stage according to Sto¨ber method. The PMBAAm shell was then encapsulated over the silica core by distillationeprecipitation polymerization of N,N0-methylenebisacrylamide (MBAAm) in neat acetonitrile with 2,20-azobisisobutyronitrile (AIBN) as initiator. The encapsulation of PMBAAmon silica particles was driven by the hydrogen-bonding interaction between the hydroxyl group on the surface of silica core and the amide unit of PMBAAm during the polymerization without modification of the silica surface in the absence of any stabilizer or surfactant. The shell thickness of the coreeshell composite particle was controlled via altering the mass ratio of MBAAm monomer to silica core during the polymerization. Hollow PMBAAm microsphere was further developed after removal of silica core with hydrofluoric acid. The resultant core-shell composite and hollow microspheres were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier-transform infrared spectra (FT-IR) and elemental analysis (EA).