作者：Feng Bai, Xinlin Yang, Wenqiang Huang*,
关键字：Distillation precipitation polymerization; Polydivinylbenzene; Microspheres
论文来源：期刊
具体来源：Macromolecules, 37 (26), 9746-9752 (2004). DOI: 10.1021/ma04
发表时间：2004年
Highly cross-linked narrow or monodisperse poly(divinylbenzene) (PDVB) microspheres were prepared by distillation-precipitation polymerization as a novel polymerization echnique in acetonitrile with 2,2￠-azobis(2-methylpropionitrile) (AIBN) as initiator. The polymeric microspheres were formed simultaneously through a precipitation polymerization manner during the distillation of acetonitrile off the reaction system. Narrow or monodisperse particles with spherical shape and smooth surface were prepared with diameters between 1.10 and 3.41 ím without any stabilizers. The particle size and size distribution depended on the reaction conditions. The maximum particle size of 2.14 ím with size distribution index of 1.058 was attained at cross-linking degree of 64%, and the size distribution became narrower with increasing cross-linking degree. The particle sizes increased with increasing monomer and initiator concentration. A series of polymer particles with diameter between 1.99 and 3.41 ím were obtained by multi-semibatch mode with successive introduction of a mixture of the designed amount of AIBN and divinylbenzene containing 80% divinylbenzene (DVB80) in acetonitrile into the distillation precipitation polymerization, and the size distribution index was kept around 1.02. Furthermore, the conversion increased from 31% for the first aliquot to 76% for the sixth aliquot. All of the resulting microspheres were characterized with SEM.