Fabric electrodes coated with polypyrrole nanorods for flexible supercapacitor application prepared via a reactive self-degraded template
作者：Jie Xu*, Daxiang Wang, Lingling Fan, Ye Yuan, Wei Wei, Ruina Liu, Shaojin Gu, Weilin Xu*
关键字：Polypyrrole nanorods，Fabric electrode
论文来源：期刊
具体来源：Organic Electronics
发表时间：2015年
Wearable energy storage devices that can be used in the garment industry are strongly required to power E-textiles. In this article, polypyrrole (PPy) nanorods were deposited on cotton fabrics via in situ polymerization of pyrrole in the presence of the fibrillar complex of FeCl3 and methyl orange as a reactive self-degraded template. The obtained fabrics could be directly used as supercapacitor electrodes, with a maximum specific capacitance of 325 F g1 and an energy density of 24.7 Wh kg1 at a current density of 0.6 mA cm2. The capacitance remained higher than 200 F g1 after 500 cycles.