作者：Ming Luo, Xing-Hong Zhang*, Bin-Yang Du, Qi Wang, Zhi-Qiang Fan
关键字：Carbonyl sulfide，Cyclohexene oxide，Copolymerization
论文来源：期刊
具体来源：Polymer 55 (2014) 3688-3695
发表时间：2014年

This paper describes the first example of alternating copolymerization of carbonyl sulfide (COS) with cyclohexene oxide (CHO) via heterogenous catalysis of a nano-lamellar zincecobalt(III) double metal cyanide complex (ZneCo(III) DMCC), providing an efficient method for converting COS to poly(cyclohexene monothiocarbonate) (PCHMTC) with an alternating degree up to 93%. The number-average molecular weight (Mn) of PCHMTC was 6.5e25.0 kg/mol with polydispersities (PDIs) of 1.6e2.1. The productivity of the catalyst was up to 970 g polymer/g catalyst (5.0 h). The oxygenesulfur exchange reaction (O/S ER) caused by ZneCo(III) DMCC was largely suppressed when the reaction was performed at 100e110
C in the presence of THF or CH2Cl2, and thus the selectivity of the monothiocarbonate over carbonate linkages was up to 98%. The mechanisms of the copolymerization and O/S ER were proposed based on the ESI-MS, GCeMS and FT-IR spectra. The obtained PCHMTC is highly transparent and exhibitsgood solubility in various organic solvents, high Tg of 112
C, initial decomposition temperature of 214
C and high refractive index of 1.705.