作者：Zhang JC, Zhang H, Wu LB, Ding JD
关键字：Paraffin spheres，Particulate leaching technique ，pore interconnectivity
论文来源：期刊
具体来源：Journal of Materials Science 41 (6): 1725-1731 2006.3
发表时间：2006年

This paper reports polymeric scaffolds with spherical internal macropores and relatively large external dimension. Paraffin spheres with the diameter of several hundred microns were prepared by a suspension technique. Particulate leaching technique based on this kind of spherical porogens was combined with room-temperature compression molding technique to fabricate biodegradable poly(D,L-lactic-co-glycolic acid) (PLGA) porous scaffolds potentially for tissue engineering or in situ tissue induction. The scaffolds exhibited ordered macropores with good pore interconnectivity. The porosity ranged from 80 to 97% adjusted simply by varying porogen content. The foams with porosity around 90% have compressive modulus over 3 MPa and compressive strength over 0.2 MPa. As preliminary cell experiments with 3T3 fibroblasts cultured on the porous scaffolds indicate, the processing procedure of the scaffolds has not brought with problem in cytotoxicity.