作者：Junchuan Zhang, Linbo Wu, Dianying Jing, Jiandong Ding*
关键字：Tissue engineering，Porous scaffolds， Biodegradable polymer
论文来源：期刊
具体来源：Polymer 46: 4979–4985 (2005.6)
发表时间：2005年

Two kinds of polyester porous scaffolds having cubic and spherical macropores were fabricated, and a comparative study of their morphologies and mechanical properties were made in this paper.Poly(D,L-lactic-co-glycolicacid)(PLGA) scaffolds were prepared by room temperature compression molding and particulate leaching method based on cubic NaCl particles and paraffin spheres with a similar size
range of 355–450mm and a series of porosities (77–97%). Scanning electronic microscopy demonstrated that the spherical pore scaffolds exhibited better pore interconnectivity than the cubic pore ones. In compressive tests of both kinds of scaffolds, striking yield peaks were found at relatively low porosities, but just non-linear flexure behavior was observed at high porosities. The power-law relationships of compressive modulus and compressive strength versus porosity were confirmed in both foams. Comparison of the underlying scaling exponents reveals that the scaffolds with spherical pores are, at high porosities, with better compressive properties to a certain degree in contrast to those with cubic pores.