Viscoelastic Properties of Polyarylene ether nitriles/Thermotropic Liquid Crystalline Polymer Blend. Journal of Applied Polymer Science, 2008, 108, 1934-1941.
作者:Defeng Wu, Yisheng Zhang, Lanfeng Wu, Lifeng Jin, Ming Zhang, Weidong Zhou, Changhao Yan.
关键字:polyarylene ether nitriles; thermotropic liquid crystalline polymer; blend; rheology.
论文来源:期刊
具体来源:Journal of Applied Polymer Science
发表时间:2008年

Journal of Applied Polymer Science, 2008, 108, 1934-1941.

ABSTRACT:

Polyarylene ether nitriles (PEN)/thermotropic liquid crystalline polymer (TLCP) blend was prepared via melt mixing. The immiscible phase morphologies, linear and non-linear as well as transient viscoelastic properties of the blend were studied using SEM, rheometer and DMA. The linear dynamic viscoelastic behavior of the blend shows temperature dependence due to further evolution of the immiscible morphology and, as a result, the principle of time-temperature superposition (TTS) is invalid. In the steady shear flow, the discrete TLCP phase is difficult to be broken up due to the high viscosity ratio of the blend systems, while is easy to be coarsened and followed by elongation and finally, to form fibrous morphology at high TLCP content and high shear level. During this morphological evolution process, the transient stress response presents step increase and non-zero residual relaxation behavior, leading to increase of the dynamic viscoelastic responses after steady preshear.

PDF DOWNLOAD:

http://www3.interscience.wiley.com/journal/117901643/abstract