Poly(phenylene sulfide) Magnetic Composites. I. Relations of Percolation between Rheology, Electrical and Magnetic Properties. Journal of Polymer Science Part B: Polymer Physics, 2008, 46, 233-243.
作者:Defeng Wu, Lanfeng Wu, Fei Gao, Ming Zhang, Changhao Yan, Weidong Zhou.
关键字:poly(phenylene sulfide); ferrosoferric oxide; composites; percolation; magnitic property.
论文来源:期刊
具体来源:Journal of Polymer Science Part B: Polymer Physics
发表时间:2008年
Journal of Polymer Science Part B: Polymer Physics, 2008, 46, 233-243.
ABSTRACT:
Poly(phenylene sulfide)/ferrosoferric oxide composites (PPS/Fe3O4) with various loading levels were prepared by melt compounding. The microstructure of composites was investigated using SEM and XRD. The rheological, electrical and magnetic properties were characterized respectively by the parallel plate rheometer, high resistance meter and magnetometer. The results reveal that the Fe3O4 particles are well dispersed in the PPS matrix due to their nice affinity, which results in a weak strain overshoot at large amplitude oscillatory level. Both the rheological and the electrical responses of the composites show a typical percolation behavior. But the rheological percolation presents lower threshold (<40wt%) than that of electrical percolation (~50wt%), which is attributed to the difference structure of the percolation network. The magnetic response, however, shows good linear relation with Fe3O4 loadings, indicating that the physical percolation has little influence on the magnetic properties. This is mainly due to the yielded long-range magnetic interactions among Fe3O4 particles in the applied field, which are far stronger than those non-magnetic physical interactions accounting for percolation.
PDF DOWNLOAD:
http://www3.interscience.wiley.com/journal/117868189/abstract