65. Dendritic-to-faceted crystal pattern transition of ultrathin poly(ethylene oxide) films
作者:Guoliang Zhang, Liuxin Jin, Zhenpeng Ma, Xuemei Zhai, Miao Yang, Wei Wang*, and Gerhard Wegner
关键字:Crystal pattern; Dendritic-to-faceted; Poly(ethylene oxide)
论文来源:期刊
具体来源:The Journal of Chemical Physics
发表时间:2008年

The detailed Tc-sensitive crystal pattern transition from dendrites through fourfold-symmetric structures to faceted crystals of ultrathin poly(ethylene oxide) films has been experimentally observed using atomic force microscopy. The transition has been quantitatively described by the Tc-dependences of the fractal dimension and of the velocity ratio caused by forward and transverse growths in crystal tips. The essential aspect of the pattern selection and transition is mainly the competition of two macroscopic mechanisms: Nucleation-limited and diffusion-limited growths which create faceted and dendritic crystal patterns, respectively. Their combination is a facet growth within a diffusion field which will create a faceted dendrite.