作者：王海
关键字：Ce3+: YAG，Phosphor-in-glass，Films，Luminescent properties
论文来源：期刊
具体来源：Journal of Alloys and Compounds,
发表时间：2017年
Ce3+: Y3Al5O12 (Ce-YAG) phosphors-in-glass (PiG), which serves as both luminescent convertor and encapsulating material in the remote white light-emitting diodes (LEDs), has become a promising research field. However, the challenges in processing and mechanical strength still remain due to its submillimeter thickness. Herein, a novel transparent Ce-YAG PiG thick filmwas coated on a common glass substrate through conventional screen printing process and subsequent heat treatment. The introduced commercial Ce-YAG phosphors almost kept intact in a lead-free glass matrix. The microstructures and luminescent properties of as-prepared samples were investigated systematically. White LED device was also fabricated via mounting the optimal sample on the InGaN blue-emitting chips, which yielded bright white light with considerable luminous efficiency and color quality. The resulting screen-printed Ce-YAG PiG thick film will be a promising candidate for applications in the high-power remote white LEDs.