作者：tang rp, et al
关键字：electroluminescence
论文来源：期刊
具体来源：Polymer
发表时间：2005年
Two dendronized poly(p-phenylene vinylene) (PPV) derivatives, ED-PPV and BB-PPV, have been successfully synthesized according to the Gilch route. The obtained polymers possess excellent solubility in common solvents, good thermal stability with 5% weight loss temperature of more than 340 8C. The weight-average molecular weight (Mw) and polydispersity index (PDI) of ED-PPV and BB-PPV are in the range of (1.26–2.34)!105 and 1.37–1.45, respectively. Polymer light-emitting diodes (PLEDs) with the configuration of ITO/PEDOT:PSS/polymer/Ca/Al devices were fabricated, and the PLEDs emitted green–yellow light. The turn-on voltages of the PLEDs based on ED-PPV and BB-PPV were approximately 4.3, and 4.5 V, respectively. The PLED devices of ED-PPV exhibited the
maximum luminance of about 157 cd/m2 at 10.5 V. Photovoltaic cells with the configuration of ITO/PEDOT:PSS/polymer:C60 (1:1)/Al were also fabricated, and the energy conversion efficiency of the devices based on ED-PPV and BB-PPV was measured to be 0.58, and 0.014%, respectively, under the white light at 75 mW/cm2.