作者：Wang W, Liu RG*, Liu WL, Tan JJ, Liu WY, Kang HL, Huang Y*
关键字：LONG-RANGE ORDER; DRUG-DELIVERY; MAGNETIC-FIELD; TEMPLATES; ACID; NANOPARTICLES; SEPARATION; SYSTEM; MACROSTRUCTURES; DERIVATIVES
论文来源：期刊
具体来源：Journal of Materials Science 2010, 45(20), 5567-5573
发表时间：2010年

Porous silica with hierarchical structures was prepared from ethyl-cyanoethyl cellulose/poly(3-(methacryloyloxy)propyl-trimethoxysilane) (E-CE)C/P(MPTOS) composites with fixed cholesteric liquid crystalline (LC) phase. The scanning and transmission electron microscopy (SEM and TEM) and N-2 sorption measurements results indicate that the silica prepared from cholesteric LC composites is of hierarchical macro-, meso- and micro-porous structures, and the average pore size of the silica can be tailored by the content of the cholesteric LC phase in the (E-CE)C/P(MPTOS) composites. The resultant silicas have high specific surface area with the highest value of 837 m(2)/g at the pore volume of 0.83 cm(3)/g. This approach provides a new choice for the preparation of porous silica materials, especially from the templates that are not compatible with aqueous system.