作者：Dongming Qi*, Zhijie Chen, Lei Yang, Zhihai Cao, Minghua Wu
关键字：miniemulsion technique, latex film, pigment
论文来源：期刊
具体来源：Advances in Materials Science and Engineering, 2013, Article ID 790321, 6 pages
发表时间：2013年
Three primary pigment/poly(n-butyl acrylate-co-styrene) (P(BA+St)) nanocomposites were prepared via encapsulation of the corresponding organic pigments via the miniemulsion technique. The resulting latexes of the P(BA+St)/pigment nanocomposites were filmed in a PTFE mould or printed onto cotton fabric. The morphology of the P(BA+St)/pigment nanocomposites, and the dispersion of pigment particles in the latex film, and on the printed fabric surface, as well as the adhesion between pigment and adhesive film were evaluated by transmission electron microscopy (TEM), field emission scanning electron microscopy (FESEM), 3D digital microscope system (3D-POM), and printing results tests. Attributing to the pre-protection of adhesive polymer shell, the self-adhesive P(BA+St)/pigment nanocomposites were homogeneously and firmly dispersed both in the thin latex film and in the adhesive layer on the fiber surface. As a result, the color strength, color fastness, and handle of the fabrics printed by the P(BA+St)/pigment nanocomposites latex were significantly improved, compared to the fabrics printed by the conventional pigment blended latex.