作者：Dong-ming Qi, Yong-zhong Bao, Zhi-ming Huang, Zhi-xue Weng
关键字：Miniemulsion polymerization, Nanocomposite, Encapsulation
论文来源：期刊
具体来源：polymer, 47: 4622-4629
发表时间：2006年

Acrylate polymer/silica nanocomposite particles were prepared through miniemulsion polymerization by using of methyl methacrylate/butyl acrylate mixture containing the well-dispersed nanometer-sized silica particles coupled with 3-(trimethoxysilyl)propyl methacrylate (MPS). The encapsulation efficiency of silica particles were determined through the elution and hydrofluoride acid etching experiments, and the size distribution and the morphology of the composite latex particles were characterized by dynamic light scattering (DLS) and transmission electron microscopy (TEM). The coupling treatment of silica with MPS can improve the encapsulation efficiency of silica and the grafting degree of polymer onto silica. When 0.10g MPS/g silica was used to modify silica, the encapsulation efficiency of silica was greater than 95%, and the grafting degree of acrylate polymer onto silica was about 60%. Although the average size and the size distribution index of the composite latex particles increased as the weight fraction of silica increased, the stable latex containing the “guava-like” composite particles was obtained. The grafting of polymer onto silica particles improved the dispersing degree of silica particles in the solvents for acrylate polymer and in the polymer matrix.