作者：Dongming QI, Lei YANG, Minghua WU, Heming LIN and Kohhei NITTA
关键字：rigid organic filler, polypropylene, dispersion, in-situ formation
论文来源：期刊
具体来源：Front. Chem. Eng. China, 2(3): 236-241
发表时间：2008年

A novel phenolic rigid organic filler (KT) was melt-mixed with an isotactic polypropylene (iPP) to prepare a series of PP/KT composites, with or without maleic anhydride grafted polypropylene (MAPP) as compatilizer. The evolution of filler morphology during melt-mixing and melt-pressure processes was monitored by scanning electron microscope (SEM) and polarized optical microscope (POM). The influences of shear force, pressure time, filler content and MAPP concentration on the final filler dispersion were studied. We found that this rigid organic filler readily melted and dispersed homogenously into the iPP matrix through a fission-fusion process during the melt-mixing process. Thus a balanced dispersion, which was closely related to shear force and MAPP concentration, can be achieved. During the melt-pressure process, parts of the filler particles combined gradually through a coalescence process. However, the incorporation of MAPP can effectively inhibit the tendency to coalesce and refine the filler particles sizes into nanoscale. Thus, a series of PP/KT composites with controllable filler particles size and narrow size distribution can be obtained just by adjusting process conditions and MAPP concentration. In addition, due to the in-situ formation mechanism, the filler phase possessed a typical solid true-spherical shape.