作者：Xie Qin, Liu Zhaoping, Shao Mingwang, Kong Lingfen, Yu Weichao, Qian Yitai*
关键字：Crystal morphology, Hydrothermal crystal growth; A2. Single crystal growth, Nanomaterials, Polymers, Semiconducting materials
论文来源：期刊
具体来源：J. Crystal Growth 2003, 252, 570-574.
发表时间：2003年

Sb₂Se₃ nanoribbons have been prepared by a hydrothermal process at 180°C for 20 h. X-ray diffraction pattern indicates that the product was orthorhombic Sb₂Se₃ phase with lattice constants a=11.747, b=11.799 and c=3.987 Å. Field emission scanning electron microscope images show that nanoribbons have diameters in the range of 25–100 nm and lengths up to 30 μm. High-resolution transmission electron microscopy image reveals that the nanoribbon was of single crystal and grew along the [0 0 1] direction. The peak of absorption appeared at 727 nm in the UV-vis spectrum. A possible mechanism on the formation of the nanostructures was also discussed.