作者：Zhaoping Liu, Sheng Peng, Qin Xie, Zhaokang Hu, You Yang, Shuyuan Zhang, Yitai Qian*
关键字：Bismuth sulfide, Nanoribbons, Inorganic
论文来源：期刊
具体来源：Adv. Mater. 2003, 15, 936-940.
发表时间：2003年
Ultralong Bi2S3 nanoribbons have been synthesized by a solvothermal process, using a mixture of aqueous NaOH solution and glycerol as the solvent. These nanoribbons (see Figure) are 50–300 nm wide, 20–80 nm thick, and up to several millimeters long, and the initial formation of the precursor polycrystalline NaBiS2 phase is crucial to their formation. The nucleation and growth process was interpreted as a solid–solution–solid transformation.