作者：F. L. Lai, Y. P. Huang, Y. E. Miao, T. X. Liu*
关键字：nickel-cobalt layered double hydroxides, hierarchical nanostructure, electrospinning, carbon nanofiber membrane, supercapacitors.
论文来源：期刊
具体来源：Electrochimica Acta, 2015, 174, 456-463.
发表时间：2015年
Hybrid nanomaterials with hierarchical structures have been considered as one kind of the most promising electrode materials for high-performance supercapacitors with high capacity and long cycle lifetime. In this work, multi-dimensional hybrid materials of nickel-cobalt layered double hydroxide (Ni-Co LDH) nanorods/nanosheets on carbon nanofibers (CNFs) were prepared by electrospinning technique combined with one-step solution co-deposition method. Carbon nanofiber membranes were obtained by electrospinning of polyacrylonitrile (PAN) followed by pre-oxidation and carbonization. The successful growth of Ni-Co LDH with different morphologies on CNF membrane by using two kinds of auxiliary agents reveals the simplicity and universality of this method. The uniform and immense growth of Ni-Co LDH on CNFs significantly improves its dispersion and distribution. Meanwhile the hierarchical structure of carbon nanofiber@nickel-cobalt layered double hydroxide nanorods/nanosheets (CNF@Ni-Co LDH NR/NS) hybrid membranes provide not only more active sites for electrochemical reaction but also more
efficient pathways for electron transport. Galvanostatic charge-discharge measurements reveal high specific capacitances of 1378.2 F g^-
1 and 1195.4 F g^-
1 (based on Ni-Co LDH mass) at 1 A g
^-1 for CNF@Ni-Co LDH NR and CNF@Ni-Co LDH NS hybrid membranes, respectively. Moreover, cycling stabilities for both hybrid membranes are significantly enhanced compared with those of Ni-Co LDH NR and NS powders. This facile method provides a new strategy for designs and applications of binary transition metal oxides/
hydroxides deposited on various substrates for next-generation energy storage devices.