作者：L. L. Ren, S. Huang, W. Fan, T. X. Liu*
关键字：Graphene, Superparamagnetic, Iron oxide, Hydrothermal
论文来源：期刊
具体来源：Applied Surface Science, 2011, 258(3), 1132-1138.
发表时间：2011年

In  this  paper,  graphene/magnetite  composites  with  hierarchical  Fe3O4 structures  were  synthesized  via a  one-step  hydrothermal  method.  The  size  of  Fe3O4 nanocrystals  and  nanocrystal  clusters  can  easily  be  controlled  by  altering  reaction  time  and  the  starting  mixed  solvent  ratio,  respectively.  Raman
measurements  evidenced  that  graphene  oxide  was  simultaneously  reduced  to  graphene  during  the  deposition  of  magnetite  particles.  The  deposition  of  Fe3O4 nanocrystals  and  nanocrystal  clusters  impedes graphene  to  restore  the  graphite  structure.  The  composites  showed  a  high  crystallinity  of  magnetite  and a
considerable saturation magnetization. Furthermore, the acrylate modified Fe3O4 makes the composites  water-dispersible  and  can  effectively  load  polyfluorene  polyelectrolyte  via  electrostatic  force.  The high magnetism, excellent water
dispersibility and strong photoluminescence make these composites ideal  candidates  for  various  important  applications  such  as  magnetic  resonance  imaging,  bioseparation, bioimaging,  and  optical  devices  fabrication.