Journal Applied Polymer Science 1998, 70(8), 1427-1436
作者:Lang, Meidong; Zhang, Guo; Chen, Xinfang; Feng, Na; Li, Shuhua
关键字:amphiphilic block copolymers; emulsifying volume; crystallinity; phase transfer catalytic property; solvent cast film
论文来源:期刊
发表时间:1998年

Poly(ethylene glycol)-block-poly(butyl acrylate) synthesized by radical polymerization in a one-step procedure were characterized by gel permeation chromatography, infrared, 1H-NMR spectroscopy, and differential scanning calorimetry (DSC). The crystalline property, emulsifying property, and phase transfer catalytic effect in the Williamson reaction were studied. It was found that the crystallinity of the copolymer increased with an increase in both the content and molecular weight of poly(ethylene oxide) (PEO) sequences. DSC curves showed two distinct crystallization temperature due to the heterogeneous nucleation and homogeneous nucleation crystallization. The casting solvent significantly affected the morphology and crystallinity of the solvent cast films. Both the emulsifying volume and the phase transfer catalytic efficiency in the Williamson reaction increased with the amount and PEO content of the block copolymers used, but decreased with an increase in the molecular weight of PEO sequences.