【Langmuir 】A New Three-Dimensional (3D) Multilayer Organic Material: Synthesis, Swelling, Exfoliation, and Application
作者:Xu Lu; Huang Youju; Li Junjun; Wang Daoliang; Chen Mingming; Tao Jiaojiao; Cui Kunpeng; Pan Guoqian*
关键字:Three-Dimensional (3D) Multilayer Organic Material
论文来源:期刊
具体来源:Langmuir 2013, 29, 3813?3820
发表时间:2013年
A novel fully rigid, rod-shaped oligo(p-benzamide) (OPBA-6) molecule was designed and synthesized, which can be recrystallized into a three-dimensional (3D) multilayer material via an antiparallel molecular packing model. Intermolecular hydrogen bonding and π?π interaction are brought to ensure a strong intralayer interaction, while decoration of layer surface with sulfonic groups promotes water to enter interlayer space and facilitates the swelling and exfoliation of sample. With a simple dispersion in water, the obtained multilayer material can be easily swollen by water without destruction of in-plane morphology and subsequently delaminated into 2D nanosheets with thickness of about 5.38 nm. This achievement may be the first attempt to exfoliate layered organic materials and thus provide a new strategy to prepare 2D organic nanosheets without using any substrates or templates as required by conventional and widely used selfassembly routes. Based on exfoliated nanosheets, poly(vinyl alcohol) nanocomposites were prepared using a simple water solution processing method. A 64% increase in tensile stress and a 63% improvement in Young’s modulus were achieved by addition of 7 wt % OPBA-6 loading.