Preparation of well-de?ned blackberry-like polypyrrole/?y ash composite microspheres and their electrical conductivity and magnetic properties
作者:Chao Yang, Tingmei Wang, Peng Liu
关键字:Polypyrrole,Fly ash,Blackberry-like morphology,Magnetic properties
论文来源:期刊
具体来源:Current Opinion in Solid State and Materials Science
发表时间:2011年

Composites consisting of conducting polypyrrole (PPy) and ?y ash (FA) or amino-functionalized ?y ash
(A-FA) were prepared by the in situ chemical oxidative polymerization method, respectively. The surface
functionalization of ?y ash (FA) with amino groups was found to play an important role in the formation
of the well-de?ned blackberry morphology. The scanning electron microscopy (SEM) analysis showed
that the well-de?ned blackberry-like morphology of the polypyrrole/amino-functionalized ?y ash
(PPy/A-FA) composites with size range of 0.3–5 lm and the surface of the composites became smoother
with more A-FA charged in the in situ chemical oxidative polymerization. X-ray diffraction (XRD) analysis
of the PPy/A-FA composites showed the similar patterns as FA, which revealed that the crystal structure
of FA was well-maintained after the surface functionalization and the in situ chemical oxidative polymer-
ization. Thermogravimetric analysis (TGA) showed that the thermal stability of PPy/A-FA composites was
enhanced and this could be attributed to the retardation effect of amine-functionalized ?y ashes as bar-
riers for the degradation of polypyrrole. The composites possess high electrical conductivity at room tem-
perature, weak temperature dependence of the conductivity and good magnetic properties.