作者：Ying Song, Hongyan Yao, Haiwei Tan, Shiyang Zhu, Bo Dong, Shaowei Guan
关键字：hyperbranched polyimide,memory behavior
论文来源：期刊
具体来源：DYES AND PIGMENTS,2017,139,730-736
发表时间：2017年
Three aromatics endcapped hyperbranched polyimides (HBPIs), with triphenylamine derivative (A3) as core, 4,4-(hexafluoroisopropylidene)diphthalic anhydride as B-2 monomer, phthalic anhydride (PA), 1,8Naphthalic anhydride (NA) and 3,4-perylenedicarboxylic anhydride (PDA) as endcapping reagents are explored as polymer memory materials. All these HBPIs showed excellent solubility in various organic solutions. Tunable memory characteristics from volatile to nonvolatile were obtained by adjusting the endcapping groups. Compared to PA endcapped HBPI, NA and PDA endcapped HBPIs exhibited enhanced nonvolatile memory behaviors with switch voltages low to 0.8 V and 1.0 V, and outstanding thermal stability with 5% weight loss temperatures reaching up to 533 degrees C and 554 degrees C, respectively. Such superior performance can be attributed to the introduced polycyclic arenes end-groups, which leads to stronger conjugation intensity, better hole transport ability and higher charge separation stability.