Functionalization of multi-wall carbon nanotubes to reduce the coefficient of the friction and improve the wear resistance of multi-wall carbon nanotube/epoxy composites
作者：Li-Jun Cui, Hong-Zhang Geng , Wen-Yi Wang, Li-Ting Chen, Jing Gao
关键字：Functionalization, multi-wall carbon nanotubes, coefficient of the friction, wear resistance, multi-wall carbon nanotube/epoxy composites
论文来源：期刊
具体来源：CARBON 54 (2013) 277–282
发表时间：2012年
Functionalization of multi-wall carbon nanotubes (MWCNTs) was achieved by grafting carboxyl groups and amino groups. Fourier transform infrared spectroscopy was used to detect the changes produced by functional groups on the surface of the MWCNTs. Three different MWCNTs were incorporated into epoxy resin and the friction and wear behavior of MWCNT/epoxy composites was investigated using a M-2000 wear testing machine at different sliding speeds under different applied loads. Scanning electron microscopy was used to observe the worn surfaces of the samples. The results indicated that the functional groups had been grafted on the surface of MWCNTs. Compared with neat epoxy, the composites with MWCNTs showed a lower friction coefficient and wear rate, and the wear rate decreased with the increase of MWCNT loading. Combining epoxy resin with MWCNTs is an efficient method to improve the wear resistance and decrease the coefficient of friction.