作者：Yufen Li,a,b,? Yuanna Sun,a,? Ying Xiao,a Guorong Gao,a Shuhui Liu,a Jianfeng Zhang,b and Jun Fua,*
关键字：Micelles, tough, hydrogels, electric- field, electroactive
论文来源：期刊
具体来源：ACS Applied Materials and Interfaces
发表时间：2016年

Multi-responsive polyelectrolyte hydrogels with extraordinary toughness have great potential in soft device applications. Previously we have demonstrated a series of tough and multi-responsive hydrogels by using multi-functional triblock copolymer (Pluronic F127 diacrylate, F127DA) micelles to crosslink cationic polyelectrolyte chains into 3D network. Herein, we further synthesize negatively charged hydrogels comprised of 2-acrylamido-2-methyl propylsulfonic acid (AMPS) monomers by using F127DA micelles as crosslinkers. Similar to the positive nanomicelle (NM) hydrogels, the negative NM hydrogels exhibited a compressive strength up to 59 MPa with a fracture strain re to 98%, and tensile fracture strain higher than 2000%. These charged hydrogels were actuated by electric field when immersed in salt solutions. The effects of electrolyte concentration, electric field strength and ionic monomer content on the electric actuation behavior of these electroactive hydrogels (EAHs) have been systematically investigated. It is concluded that the electroactive hydrogel show a fast actuation rate with a bending angle up to 87° at 120 s and the bending angle was cyclically reversed upon changing bias direction without large decrease. This study demonstrates that such tough and multi-responsive electroactive hydrogels may have great potentials in sensors, actuators, switches, and

artificial muscles.