作者：Fu, J.; Ghali, B. W.; Lozynsky, A. J.; Oral, E.; Muratoglu, O. K.
关键字：High temperature melting, wear, total joint implants
论文来源：期刊
具体来源：Polymer, 2010, 51, 2721-2731
发表时间：2010年

Our goal was to improve the strength and toughness of ultra high molecular weight polyethylene (UHWMPE), which is the preferred polymeric bearing material in total joint implants. Based on accelerated diffusion of UHMWPE chains at high temperatures, our hypothesis was that high temperature melting could minimize the structural defects and thus improve the toughness of consolidated UHMWPE. Melting of consolidated medical-grade UHMWPE at 280, 300, and 320 ^oC in inert atmosphere improved the elongation at break, work-to-failure and impact strength, presumably due to chain scissioning and structural defect elimination through self-diffusion. An important finding of this study was that the gain in plasticity and toughness did not sacrifice the wear resistance under optimized melting conditions, which may be promising for next generation high performance UHMWPE materials for joint implant bearing surfaces.