Langmuir, 2012,28, 3011-3017: Water-dispersible, uniform nanospheres via heating-enabled micellization of amphiphilic block copolymers in polar solvents
作者：Zhiming Yang, Zhaogen Wang, Xueping Yao, Yong Wang
关键字：block copolymer, nanosphere, micellization, encapsulation, selective solvent, fluorophore, quaternization
论文来源：期刊
发表时间：2012年
Uniform nanospheres with tunable size down to 30 nm were prepared simply by heating amphiphilic block copolymers in polar solvents. Unlike reverse micelles prepared in nonpolar, oily solvents, these nanospheres have a hydrophilic surface, rendering them good dispersibility in water. Furthermore, they are present as individual, separated, rigid particles upon casting from the solution other than continuous thin films of merged micelles cast from micellar solution in nonpolar solvents. These nanospheres were generated by a heating-enabled micellization process in which the affinity between the solvent and the polymer chains as well as the segmental mobility of both hydrophilic and hydrophobic blocks was enhanced, triggering the micellization of the glassy copolymers in polar solvents. This heating-enabled micellization produces purely well-defined nanospheres without interference of other morphologies. The micelle sizes and corona thickness are tunable mainly by changing the lengths of the hydrophobic and hydrophilic blocks, respectively. The heating-enabled micellization route for the preparation of polymeric nanospheres is extremely simple, and is particularly advantageous in producing rigid, micellar nanospheres from block copolymers with long glassy, hydrophobic blocks which are otherwise difficult to prepare with a high efficiency and purity. Furthermore, encapsulation of hydrophobic molecules, e.g. dyes, into micelle cores could be integrated into the heating-enabled micellization, leading to a simple and effective process for dye-labeled nanoparticles and drug carriers.