作者：Tao Zhang, Yunhao Du, René Schubel, Tao Chen, Dietrich R.T. Zahn, Rainer Jordan
关键字：Polymer Brushes, Wafer-scale Synthesis
论文来源：期刊
具体来源：Polymer Chemistry, 2015, 6, 8176-8183
发表时间：2015年
A method is presented that allows for the first time the preparation of highly defined polymer brush coatings on the wafer-scale under ambient conditions (room temperature, exposure to air) from a broad variety of monomers. The discovered high oxygen-tolerance of the surface-initiated Cu(0)-mediated controlled radical polymerization (SI-CuCRP) yields entire wafers homogeneously covered by a polymer brush of linear, high molar mass polymers with narrow dispersities (? = 1.1) at extremely high grafting densities
(≈ 1 chain/nm2). The low-tech and air tolerant method requires only ?4 mL reaction solution containing a monomer and a ligand between two facing substrates. Thus, the SI-CuCRP is scalable to any surface area with minimal costs and minimal equipment. Despite the simplicity of the method, the high endgroup fidelity of SI-CuCRP is demonstrated by the preparation of a tetrablock copolymer brush which is the first example of a higher order block copolymer brush prepared by any surface-initiated polymerization. Finally, we present a new facile lithographic technique, the copper plate proximity printing (CP3), which relies on the proximity of the bulk copper surface to the initiator-bearing substrate. The CP3 is resist- and development-free and transfers the copper plate profile (of a copper coin) directly into an image composed of a 3D polymer brush.