作者：Gao Aihuan,Pi Pihui, Wen Xiufang,Zheng Dafeng, Cai Zhiqi,Cheng Jiang,Yang Zhuoru
关键字：Metals, Pigments,Corrosion resistance, Anticorrosion, Resins, Aluminium, Organic-inorganic,Sol-gel, One-step encapsulation, Colour lightness difference
论文来源：期刊
具体来源：PIGMENT & RESIN TECHNOLOGY卷: 41 期: 3 页: 149-155 DOI: 10.1108/03699421211226435
发表时间：2012年
Purpose - The purpose of this paper is to enhance the anticorrosion property of aluminium pigments and to improve their compatibility with polymers in coating. Design/methodology/approach - Aluminium pigments encapsulated by organic-inorganic layer were prepared by hydrolysis and condensation of organic silane acrylate resin and tetraethoxy silane (TEOS) on the surface of pigments via sol-gel method. TEOS and poly (methyl methacryalte-n-butyl acrylate-vinyl triethoxysilane) (PMBV) formed in advance by co-polymerisation of methyl methacrylate (MMA), n-butyl acrylate (BA) and vinyl triethoxysilane (VTES) were used as precursors. The adhesion property of the aluminium pigments was measured by peel test, and the loss of silvery appearance after encapsulation and acid soaking were both evaluated by colour lightness difference (Delta L) measurement. The encapsulated aluminium pigments were further characterised by means of FTIR, SEM, TG and XPS. Findings - It was found that PMBV-SiO2 thin films could be formed on the surface of aluminium pigments smoothly and uniformly, and the adhesion and anticorrosion performances of encapsulated aluminium pigments were improved significantly.Research limitations/implications - The organic silane acrylate resin used as a precursor in the sol-gel process could be synthesised from other aclyate monomers. In addition, the hydrolysis and condensation mechanism of organic silane acrylate resin on the surface of aluminium pigments need further studies. Practical implications - The method developed provided a good solution to the two problems of aluminium pigments and increased their application values. Originality/value - The method of improving adhesion and anticorrosion properties of aluminium pigments was novel and could find numerous applications in surface coatings and adhesives.