Newtonian flow behavior of high-molecular-weight hypebranched polyethylenes produced with a Pd-diimine catalyst and its dependence on chain topology
作者：Z. Ye, S. Zhu*
关键字：无
论文来源：期刊
具体来源：Macromolecules
发表时间：2003年
This work examined the rheological properties for a series of highly branched polyethylene
samples prepared with a Pd-diimine catalyst system. It was revealed that the polymers produced at low pressure (0.2 and 1 atm) and higher temperature (35 °C) exhibited rheological behavior characteristic of hyperbranched polymers. The samples had very low
viscosities and showed Newtonian flow behavior due to the absence of chain entanglements. The change of chain topology from hyperbranched to linear led to much higher viscosity and non-Newtonian flow behavior due to chain entanglements.