  • Wear-resistant and transparent acrylate-based coating with highly filled nanosilica particles
  • 来源:汤龙程副研究员个人网站 2014-11-14
  • Hybrid nanocoatings are one of the most attractive topics in nanomaterials which have achieved the transition from fundamental researches to practical applications. In the present study, a urethane–a- crylate oligomer was mixed with varied concentrations of nanosilica particle sol, spin-coated onto polycarbonate substrate and finally cured by ultraviolet (UV) rays. The morphology, mechanical properties and wear resistance of the resultant hybrid coatings were systematically investigated. Infrared spectroscopy (IR) analysis was performed to determine the eventual curing extent of the mixtures studied. The transmission electron microscopy (TEM) micrographs revealed almost perfect dispersion of the nanosilica particles within organic matrices, which ensured the excellent transparence of the hybrid coatings. Nanoindentation was further conducted to determine the mechanical properties, i.e. hardness, elastic modulus and their nanoparticle loading dependence. The short-term wear resistance was characterized by a pencil hardness tester. Moreover a universal micro-tribotester (UMT) was applied to investigate the long-term performance. As a result, about 20% decrease in coefficient of friction (COF) was achieved by the coating filled with 40 wt% nanosilica particles, compared to that of the unfilled coating. Under the same fretting test conditions, the wear rate in terms of wear volume of the hybrid coating containing 40 wt% nanoparticles was about 70 times lower than that of the neat coating, confirming the wear-reduction capability of the nanoparticles. The related wear mechanisms were discussed based on worn-surface observations. 

  • [来源:中国聚合物网]
  • 了解更多请进入: 汤龙程副研究员个人网站
相关新闻
  • · Fracture Behaviors of TRGO-Filled Epoxy Nanocomposites with Different Dispersion/Interface Levels
  • · Mechanical Properties and Fracture Behaviors of Epoxy Composites With Phase-Separation Formed Liquid Rubber and Preformed Powdered Rubber Nanoparticles: A Comparative Study
  • · Temperature dependence of creep and recovery behaviours of polymer composites filled with chemically reduced graphene oxide
  • · The Effects of Alumina Nanofillers on Mechanical PropertiesofHigh-PerformanceEpoxyResin

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017