  • (Industrial & Engineering Chemistry Research) Strategy to Prepare Core–Shell Microspheres for Laser Direct Writing on Polymers: Microemulsion Method
  • 来源:周涛教授个人网站 2023-02-06
  • In this study, new core?shell microspheres for polymer laser direct writing (LDW) were successfully designed and prepared by a facile one-step micro-emulsion method. The color-changing core-shell microsphere consists of SnO2 "core" which can absorb near-infrared (NIR) laser energy and PPO "shell" which can be easily carbonized at high temperatures. Owing to the unique core-shell structure, the SnO2@PPO microsphere remarkably enhanced the polymer LDW performance. SEM, TEM and EDS indicated microspheres were regular spheres with an average size of 15.1 μm. Raman spectroscopy and XPS revealed that the SnO2 absorbed NIR laser energy to cause instantaneous high temperatures, leading to the carbonizing of PPO shell. Thus, the color-change mechanism of polymer during NIR LDW was confirmed as the formation of amorphous carbon by high-temperature carbonization. We believe these novel microspheres will have wide applications in the field of polymer LDW. Besides, the concept of preparing core-shell microspheres by the one-step micro-emulsion method provides a new idea for designing color-changing microspheres.
  • [来源:中国聚合物网]
  • 了解更多请进入: 周涛教授个人网站
相关新闻
  • · (Chemical Engineering Journal) A mechanically soft-tissue-like organohydrogel with multi-functionalities for sensitive soft ionotronics
  • · (Industrial & Engineering Chemistry Research) Laser-Induced Selective Metallization on Polymers for Both NIR and UV Lasers: Preparing 2D and 3D Circuits
  • · (Applied Surface Science) Preparation of Liquid Metal Circuits on Flexible Polymers by Selective Laser Ablation: Essential Mechanism of Non-Conductivity in Ablation Part
  • · (Industrial & Engineering Chemistry Research) Efficient and Simple Fabrication of High-Strength and High-Conductivity Metallization Patterns on Flexible Polymer Films

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017