  • Defect-engineered MOF-808 with highly exposed Zr sites as highly efficient catalysts for catalytic transfer hydrogenation of furfural
  • 来源:赵学波教授个人网站 2022-08-26
  • The highly efficient production of furfuryl alcohol (FFA) from biomass-derived furfural (FFR) is attracting increasing attention due to its wide application in the production of value-added chemicals. Zr-based MOF-808 is promising for liquid catalytic transfer hydrogenation (CTH) of FFR to FFA in terms of possessing a great number of Lewis-acid sites. Herein, a series of defective MOF-808 (D-x-MOF-808) samples were prepared via a competitive coordination-removal strategy by modulating with benzoic acid (HBC). HBC was introduced as the temporary ligand for competing with formal ligand 1,3,5-benzenetricarboxylic acid (H3BTC) to coordinate with metal clusters and then it was removed with methanol to obtain the D-x-MOF-808. The results showed that HBC serves not only as a temporary ligand participating in the synthesis of MOF-808 to obtain defective structure but also as a modulator controlling the particle size by terminating the growth of crystals. By changing the amount of HBC addition, the degree of ligand deficiency and the number of exposed Zr sites can be well regulated. Especially, excellent performance of FFR conversion (99%), FFA selectivity (94.4%) and FFA formation rate (48.6 mmol.g(-1).h(-1)) was achieved over D-40-MOF-808 sample with 2-propanol as a hydrogen donor under mild conditions (90 degrees C, 2 h), ranking it the best among the reported catalysts. Detailed characterizations proved that the high activity of D-40-MOF-808 was jointly influenced by the high surface area, the high content of exposed Zr metal sites and ligand deficiency.
  • [来源:中国聚合物网]
  • 了解更多请进入: 赵学波教授个人网站
相关新闻
  • · One-pot synthesis of conjugated microporous polymers based on extended molecular graphenes for hydrogen storage
  • · Electrochemical Surface Restructuring of Phosphorus-Doped Carbon@MoP Electrocatalysts for Hydrogen Evolution
  • · Carbon-coated NiSe nanoparticles anchored on reduced graphene oxide: a high-rate and long-life anode for potassium-ion batteries
  • · A CoSe-C@C core-shell structure with stable potassium storage performance realized by an effective solid electrolyte interphase layer

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017