  • 祝贺王滨搏“断链-动态交联制备双重动态共价高分子”的工作被Chinese J. Polym. Sci.接收
  • 来源:马松琪教授个人网站 2024-06-03
  • Upcycling of Poly(butylene adipate-co-terephthalate) into Dual Covalent Adaptable Networks

    through Chain Breaking-Crosslinking Strategy

    Binbo Wanga, Rong Huang, Xin Wang, Tao Jiang, Yi Wang, Shuai Du, Falin Li, Jin Zhu, Songqi Ma*

    Poly(butylene adipate-co-terephthalate) (PBAT), a widely studied biodegradable material, has not effectively addressed the problem of plastic waste. Taking into consideration the cost-effectiveness, upcycling PBAT should take precedence over direct composting degradation. The present work adopts a chain breaking-crosslinking strategy, upcycling PBAT into dual covalent

    adaptable networks (CANs). During the chain-breaking stage, the ammonolysis between PBAT and polyethyleneimine (PEI) established the primary crosslinked network. Subsequently, styrene maleic anhydride copolymer (SMA) reacted with the hydroxyl group, culminating in the formation of dual covalent adaptable networks. In contrast to PBAT, the PBAT-dual-CANs exhibited a notable Young''s modulus of 239 MPa, alongside an inherent resistance to creep and solvents. Owing to catalysis from neighboring carboxyl group and excess hydroxyl groups, the PBAT-dual-CANs exhibited fast stress relaxation. Additionally, they could be recycled through extrusion and hot-press reprocessing, while retaining their biodegradability. This straightforward strategy offers a solution for dealing with plastic waste.

  • [来源:中国聚合物网]
  • 了解更多请进入: 马松琪教授个人网站
相关新闻
  • · 祝贺李发林动态交联-可控溶解潜伏固化机制的工作被Macromolecules接收
  • · 祝贺杨帅琪的综述论文发表于Chem. Soc. Rev.上
  • · 祝贺杜帅“绿色高效合成二硫缩醛和聚二硫缩醛”的工作被Angew. Chem. Int. Ed.接收
  • · 课题组揭榜华为难题,荣获华为火花奖

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017