The influence of in-situ modification of silica on filler network and dynamic mechanical properties of silica-filled solution SBR
作者:Wu YouPing, Zhao QingSong, Zhao SuHe, Zhang LiQun
关键字:solution SBR,silica,in situ modification
来源:期刊
具体来源:期刊
发表时间:2008
简介:
The influence of in situ modification of silica with bis-(3-(triethoxysilyl)-propyl)-tetrasulfide (TESPT) on filler network in silica filled solution SBR compound was investigated. In situ modification greatly increased thebound rubber content. TEM observation of silica gel showed that bridging and interlocking of absorbed chains
on the surface of silica particles formed the filler network.Rubber processing analyzer (RPA) was used to characterize the filler network and interaction between silica and rubber by strain and temperature sweeps. In situ modification improved the dispersion of silica, and in the meantime, the chemical bonds were formed between silica and rubber,which conferred the stability of silica dispersion during the processing. Compared to the compound without in situ modification, the compound with in situ modification of silica exhibited higher tan d at low strains and lower tan d at high strains, which can be explained in terms of filler network in the compounds. After in situ modification,DMTA results showed silica-filled SSBR vulcanizate exhibited higher tan d in the temperature range of 230 to 108C, and RPA results showed that it had lower tan d at 608C when the strain was more than 3%.